1993 Fiscal Year Final Research Report Summary

Studies of red-, green- and blue-emitting TFEL devices using oxide phosphors

Research Project

Project/Area Number 04650024
Research Category

Grant-in-Aid for General Scientific Research (C)

Allocation TypeSingle-year Grants
Research Field Applied materials
Research InstitutionKANAZAWA INSTITUTE OF TECHNOLOGY

Principal Investigator

TAKATA Shinzo  KANAZAWA INSTITUTE OF TECHNOLOGY,DEPARTMENT OF ELECTRICAL ENGINEERING,PROFESSOR, 工学部, 教授 (70064467)

Co-Investigator(Kenkyū-buntansha) ISHII Makoto  KANAZAWA INSTITUTE OF TECHNOLOGY,DEPARTMENT OF ELECTRONICS,PROFESSOR, 工学部, 教授 (30222946)
FUKUDA Ichirou  KANAZAWA INSTITUTE OF TECHNOLOGY,DEPARTMENT OF ELECTRONICS,PROFESSOR, 工学部, 教授 (10064445)
Project Period (FY) 1992 – 1993
KeywordsElectroluminescence / EL displays / full-color EL / multicolor EL / TFEL devices / flat-panel display / barium titanate
Research Abstract

Multicolor emitting thin-film electroluminescnt (TFEL) devices using oxide-phosphor, such as Y_2O_3 : Ce (for red emission), Zn_2SiO_4 : Mn (for green, yellow, red and white), Zn_2SiO_4 : Ti (for blue), Zn_2SiO_4 : Tm (for blue), Zn_2SiO_4 : Ce (for blue-green), Sr_2P_2O_7 : Eu (for blue), Sr_2P_2O_7 : Sn (for blue), Y_2SiO_5 : Ce, BaMgAl_<14>O_<23> : Eu (for blue) and Sr_2P_2O_7 : Eu, Mn (for white) as the emitting layr are described. Red, green, blue or white emissions were obtained by controlling the preparation conditions of the emitting layr of the TFEL devices, and the compositions of the host materials for phosphors.
Results obtained are summarized as follows : 1) It was found that the oxide-phosphor emitting layrs prepared on BaTiO_3 ceramic insulating sheets postannealed at the temperature ranging from 700 to 1000゚C after deposition have good crystallinity. 2) By controlling the preparation condition and the composition of the host materials, red, green, blue and white emissions from the TFEL devices by 1 kHz sinusoidal-wave voltages were obtained with maximum luminance [in cd/m^2] of 1 for Zn_2SiO_4 : Mn, 3020 for Zn_2SiO_4 : Mn, 15.8 for Zn_2SiO_4 : Ti, respectively. 3) These hosts are promising materials as the blue, green or red emitting layr of TFEL devices, because hosts are same materials.

  • Research Products

    (3 results)

All Other

All Publications (3 results)

  • [Publications] 高田新三,南内嗣: "酸化物蛍光体を用いた薄膜EL素子" 日本学術振興会薄膜第131委員会第166回研究会資料. 166. 13-18 (1993)

    • Description
      「研究成果報告書概要(和文)」より
  • [Publications] T.Minami, K.Saikai, T.Miyata, S.Takata and T.Miyata: ""Blue-emitting TFEL devices using oxide phosphors"" Proc.13th International Display Research Conference (EuroDisplay93). 519-522 (1993)

    • Description
      「研究成果報告書概要(欧文)」より
  • [Publications] T.Miyata, T.Minami, K.Saikai and S.Takata: ""Zn_2SiO_4 as a host material for phosphor-emitting layrs of TFEL devices"" Journal of Luminescnece. 60/61. 67-70 (1994)

    • Description
      「研究成果報告書概要(欧文)」より