1994 Fiscal Year Final Research Report Summary
Study on the ultra low resistivity phenomenon of hetero structure organic thin films
| Project/Area Number |
05452182
|
|---|
| Research Category |
Grant-in-Aid for General Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Electronic materials/Electric materials
|
|---|
| Research Institution | Tohoku University |
|---|
Principal Investigator |
YAMASHITA Tsutomu Tohoku Univversity Professor, 電気通信研究所, 教授 (30006259)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
OSHIMA Shigetoshi Yamagata Univversity Professor, 工学部, 教授 (40124557)
NAKAJIMA Kensuke Tohoku Univversity Associate Professor, 電気通信研究所, 助教授 (70198084)
|
|---|
| Project Period (FY) |
1993 – 1994
|
| Keywords | LB films / Ultra low resistivity / Organic superconductor / Conductive organic thin films |
|---|
| Research Abstract |
Preparation and the electric properties of hetero structure LB films has been investigated with a view to inspect the ultra low resistivity phenomenon in the films. The ultra low resistivity has never seen in the hetero LB films of arachidic Cd (AA)/C_<15> TCNQ (TCNQ) for which Hino reported the ultra low resistivity. It has been said that the spontaneous electric field of a Z type TCNQ LB films and an electron cloud produced at the AA/TCNQ hetero interface play a important role to occur this phenomenon. Additionally, in this study, we have found that a part of TCNQ formed Cd-TCNQ complex with Cd^<2+> in a sub-phase solution and the complex could be changed to a conductive charge transfer (CT) complex. It was postulated that a two dimensional conducting layr had been formed at the interface of the non-polar AA and the polar TCNQ LB films by the Cd-TCNQ CT complex. The postulation implied us that the ultra low resistivity was probably resulted from the hetero structure of dielectric/2 d
… More
imensional conductor/dielectric on which the Ginzburg's theory of high temperature superconductivity based. In this study, we prepared conductive, polar and non-polar thin films by the LB method to realize the hetero structure and estimated film qualities and properties. Among these films, Y type arachidic Cd LB films has a sufficient films quality as the non-polar film. For conductive films, the LB films with a sufficiently high conductivity (1- S/cm) were successfully formed by use of a CT complex of BEDT-TTF (BO) and C_<15> TCNQ.For polar films, alternately deposited Y type films were fabricated instead of a labile Z type TCNQ LB films. It was found that the alternately deposited films have a sufficient quality and spontaneous electric potential of about 1.8 V for a 7 layrs film. The electric properties of the LB films with non-polar/conductive/polar hetero structure consisting of above LB films attract our attention from the application view point of new molecular devices as well as the ultra low resistivity phenomenon. Less
|