1995 Fiscal Year Final Research Report Summary
Study on blue light generation by nonlinear optical crystal KLN
| Project/Area Number |
06452133
|
|---|
| Research Category |
Grant-in-Aid for General Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Research Field |
Applied optics/Quantum optical engineering
|
|---|
| Research Institution | Osaka University |
|---|
Principal Investigator |
SASAKI Takatomo Osaka Univ., Electrical Eng., Professor, 工学部, 教授 (50029237)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
MORI Yusuke Osaka Univ., Electrical Eng., Res.Associate, 工学部, 助手 (90252618)
OHNISHI Norio ETL,Mater.Sci.Div., Senior Scientist, 材料科学部, 通産技官
HIRAKI Akio Osaka Univ., Electrical Eng., Professor, 工学部, 教授 (50029013)
|
|---|
| Project Period (FY) |
1994 – 1995
|
| Keywords | KLN fiber / blue light / nonlinear optics / second harmonics generation / single crystal / uniformity / temperature acceptance / spectral bandwidth |
|---|
| Research Abstract |
We have employed the micro-prlling down (mu-PD) method in order to overcome the difficulty in growing non-congruently melting KLN crystal of sufficient size and of reasonable umiformity of crystal composition. KLN could be formed as a small diameter fiber (200mum) with high growth rate (6mm/h) by mu-PD method. This system could make possible to grow non-congruently melting crystal with uniform conposition and high quality. Since the much smaller deviation from starting composition of the melt occurring in the growth of thinner fiber crystal, it is possible to maintain a certain composition in the solution during growth and to help in fabrication of uniform crystal in composition. Also, fewer thermal distortions and dislocations were introduced in the thinner fiber crystals. By using these fibers, we have observed blue light by frequency doubling of cw Ti : saphhire laser at RT.We have obtained 0.6mW blue output power from single pass SHG at an input power 700mW of cw Ti : Sapphire laser. The temperature and wavelength acceptances of the KLN fiber were 2.5ﾟC・cm and 0.4mm・cm at room temperature, respectively.
|