1996 Fiscal Year Final Research Report Summary
STUDIES ON ANISOTROPIC STRUCTURE AND PROPERTIES OF CO ATINGS
| Project/Area Number |
07650856
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Material processing/treatments
|
|---|
| Research Institution | FUKUI MTECHNOLOGICAL UNIVERSITY |
|---|
Principal Investigator |
MARUO Hiroshi Department of Mechanical Engineering FUKUI MTECHNOLOGICAL UNIVERSITY, 工学部, 教授 (50028982)
|
|---|
| Project Period (FY) |
1995 – 1996
|
| Keywords | Plasma sprayd coating / Deformation and solidification / Splat disc / Anisotropic structure / Sound velocity in coatings / 硬さ |
|---|
| Research Abstract |
Purpose this research project is to make clear the influence of splat accumlation on the anisotropic structure and properties of plasma sprayd coating, at the stage of spraying processing.
Experimental researches were caried out for two years, 1995-1996, results obtained are summarized as follows ;
1) Observations of splat deformation on the surface of substrate.
A group of spraying particles flying at almost same velocity were extracted from the massive spraying particle stream so as to confirm the deformation and solidification of droplet having similar velocity. State of deformation of splat on stainless steel plate substrate was observed with SEM microscope.
2) 2 Estimation of time to deform, and time to solidify of droplet on the substrate surface Molten droplet deforms to flat disc within a microsecond scale of time, and solidified after a time of millisecond order. These results were discussed theoretically.
3) Anisotropic structure and hardness of plasma sprayd coatings.
Cross sectional microscopic structure of coatins were invesigated carefully. Lamellar structure was confirmed by the vickers hardness tests.
4) Anisotropic characteristics in sound propagation
Sound velocity in perpendicular direction with respect to the zirconia coating layr, and sound velocity velocity in parallel direction were investigated with the values of 3480 m/s and 3870 m/s obtained.
5) Observation of dynamic deformation of plasma aorayd coating, with the aid of microscope.
Sprayd zirconia bending specimen, polished prior to bend, was tested under three point bending loading device. Failure of coating were hardely observed in the ellastic range of substrate materials, but brittle fracture come arise suddenly due to lack of ductility of ceramic materials.
|