1999 Fiscal Year Final Research Report Summary
FABRICATION OF LOW ABSORPTIVE AND OUTGASSING OXIDE FILM USING REACTIVE SUBCRITICAL AND SUPERCRITICAL CARBON DIOXIDE WITH OZONE.
| Project/Area Number |
09555220
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 展開研究 |
|---|
| Research Field |
Material processing/treatments
|
|---|
| Research Institution | Miyagi National College of Technology |
|---|
Principal Investigator |
MOMOSE Takashi MIYAGI NATIONAL COLLEGE OF TECHNOLOGY, ELECTRICAL ENGINEERING, PROFESSOR, 電気工学科, 教授 (90006271)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
蓼沼 克嘉 (株)化研, 水戸研究所・高度技術開発部, 代表
TATENUMA Katuyoshi MITO INSTITUTE AT KAKEN CO. LTD., DEPARTMENT OF HIGH TECHNOLOGY DEVELOPMENT, REPRESENTATIVE
|
|---|
| Project Period (FY) |
1997 – 1999
|
| Keywords | Supercritical fluid CO2 / Surface Cleaning / FTIR / Ozone treatment / Ultra High Vacuum materials |
|---|
| Research Abstract |
For the first two years, supercritical fluid (SCF) CO2 has been applied to remove native contamination on aluminum surfaces. The surface was evaluated using XPS. For this last fiscal year, SCFCO2 was applied to remove artificial contamination, triglyceride, deposited on aluminum mirror surfaces, approximately several to 20 microns thick. Contamination removing rate was evaluated with FTIR. The rate was measured using two peaks originated from CHィイD22ィエD2 and CHィイD23ィエD2 and the standard lines for the two peaks.
1. The obtained removing rate about 50 to 98 % was higher than those of the native contamination, where the rate up to 40% for the latter was evaluated using XPS. The rate obtained from the CHィイD23ィエD2 peak was higher than those from CHィイD22ィエD2 peak by amount of several to 11 %.
2. The rate is proportional to pressure of SCFCOィイD22ィエD2 in the range from 100 to 300 atm.
3. The treatment using SCFCOィイD22ィエD2 with OィイD22ィエD2 as additives resulted higher rate in average about 77% than that (66%) treated in SCFCOィイD22ィエD2 alone.
4. The lifetime was measured using OィイD23ィエD2 gas with 0.2% density. The result is : 10 hours (h) at 10 C, 4.5 h at 20-40C, 2 h at 60-70C and several ten minutes at 90C.
|