2005 Fiscal Year Final Research Report Summary
Control of Nucleation and Growth of Nanocrystal Diamond by Irradiation of Radical Low-Temperature Plasma
| Project/Area Number |
15340195
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Plasma science
|
|---|
| Research Institution | Tohoku University |
|---|
Principal Investigator |
IIZUKA Satoru Tohoku University, Graduate School of Engineering, Associate Professor, 大学院・工学研究科, 助教授 (20151227)
|
|---|
| Project Period (FY) |
2003 – 2005
|
| Keywords | nanocrystalline diamond / diamond nucleation / diamond-like carbon / electron-temperature control / low electron-temperature plasma / radical control / hydrogen methane plasma / nanowall |
|---|
| Research Abstract |
For irradiation of low-electron temperature plasma and radicals on the substrate surface, we separate electron-temperature controllable region from deposition region by orifice in inductively-coupled radio-frequency hydrogen-methane plasma. In case of 6-mm-diamter orifice, we find that nanocrystalline diamond is deposited on the substrate. Further, when the dilution ratio of methane in hydrogen is reduced to be less than 1 %, rather qualified nanocrystalline diamond is created. On the contrary, when the orifice diameter is enlarged, diamond-like carbon film is deposited. It is interpreted by a decrease in the hydrocarbon radical ratio of sp3/sp2 in the plasma. In order to apply this property on wide area film deposition, we employ a hollow-typed magnetron plasma source. A high density plasma can be produced by the effect of static magnetic and electric fields. By reducing the electron-temperature in the plasma source region, the sp2 radical density can de decreased. We find that nanoparticles with polyhedron surfaces composed by regular tetrahedron are grown in the low-electron temperature plasma. On the other hand, in high electron-temperature plasma, nanowalls made of graphite films are deposited. Such difference can be explained by the local change of sp2/sp3 components in the background film. In the low-electron temperature plasma, the ratio of sp3/sp2 becomes large, which results in the formation of nanoparticles with sp3 structure like a diamond. Damage to nucleation and growth due to energetic ions impinging on the substrate can be also reduced in the low-electron temperature plasma, where migration of reactants on the surface is promoted to produce nanoparticles with polyhedron structures.
In this way, the control of radicals in low-electron temperature plasma is quite effective for nucleation and growth of nanostructures.
|
Research Products
(19 results)