Development of highly reliable stainless steel welds and high accuracy life-prediction model based on metallography

2018 Fiscal Year Final Research Report

• Project/Area Number: 15H05564
• Research Category: Grant-in-Aid for Young Scientists (A)
• Allocation Type: Single-year Grants
• Research Field: Nuclear engineering
• Research Institution: Tohoku University
• Principal Investigator: Abe Hiroshi 東北大学, 工学研究科, 講師 (30540695)
• Project Period (FY): 2015-04-01 – 2019-03-31
• Keywords: オーステナイト系ステンレス鋼 / 溶接金属 / δ-フェライト / 応力腐食割れ / 熱時効脆化 / スピノーダル分解

Outline of Final Research Achievements

The microstructural modification method has been developed to improve SCC resistance of austenitic stainless steels. The effect of microstructural anisotropy on a thermal embrittlement of welds has been investigated.
Type 316L stainless steel in which the island-shaped delta-ferrite distribute on grain boundaries due to preferential melting and solidification by heating up to near the melting point using induction heating and then water quenched has been developed. The modified 316L stainless steel showed good SCC propagation resistance.
The Charpy absorbed energy decrease ratio with thermal aging depends only on the ferrite content, whether weld metals or cast duplex stainless steels. It has been suggested that the previous knowledge about thermal aging behavior of duplex stainless steels can be applicable for that of stainless steel welds.