2017 Fiscal Year Final Research Report
Development of lanthanum silicate electrolyte supported type SOFC single cell that operates using at 500 oC
| Project/Area Number |
15K06495
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Multi-year Fund |
|---|
| Section | 一般 |
|---|
| Research Field |
Structural/Functional materials
|
|---|
| Research Institution | Niihama National College of Technology |
|---|
Principal Investigator |
Susumu Nakayama 新居浜工業高等専門学校, 生物応用化学科, 教授 (50300637)
|
|---|
| Project Period (FY) |
2015-04-01 – 2018-03-31
|
| Keywords | 固体酸化物形燃料電池 / アパタイト |
|---|
| Outline of Final Research Achievements |
In SOFC of the electrolyte thickness 1.0 mm, the maximum power density of 29.8 mW cm-2 was able to be achieved at 500 °C. The conductivity at 500 °C of oxide ionic conductor, lanthanum silicate, of the SOFC electrolyte has improved to 0.02 S cm-1. High interfacial resistance on the electrolyte-electrode has decreased by using samarium stabilized ceria for the buffer layer.
|
| Free Research Field |
無機化学
|