2018 Fiscal Year Final Research Report
Establishment of universal design and synthesis method of functional zeolite by interzeolite conversion using a dual-template method
Project/Area Number |
16H04218
|
Research Category |
Grant-in-Aid for Scientific Research (B)
|
Allocation Type | Single-year Grants |
Section | 一般 |
Research Field |
Inorganic industrial materials
|
Research Institution | Hiroshima University |
Principal Investigator |
Sano Tsuneji 広島大学, 工学研究科, 教授 (80251974)
|
Co-Investigator(Kenkyū-buntansha) |
定金 正洋 広島大学, 工学研究科, 准教授 (10342792)
津野地 直 広島大学, 工学研究科, 助教 (40758166)
|
Project Period (FY) |
2016-04-01 – 2019-03-31
|
Keywords | ゼオライト / 水熱転換 / 有機構造規定剤 / アンモニウムカチオン / ホスホニウムカチオン / NH3-SCR |
Outline of Final Research Achievements |
We investigated syntheses of small-pore zeoliets such as CHA, AEI and AFX by a mixture of FAU zeolite with high Si/Al ratio and Al source as starting materials. It was found from ESI-MS analysis that a rapid decompsotion of high silica FAU zeolite occurred, giving locally ordered aluminosilicate speceoes (nanoparts) that assembel and evolve into another type of zeolite. Phosphorus-modified small-pore zeolites (CHA, AEI, and LEV) were also prepared by hydrothermal conversion of FAU zeolites with a mixture of an N-OSDA and P-OSDA. These P-modified zeolites exhibit a good catalytic activity and durability in the NH3-SCR process.
|
Free Research Field |
ゼオライト化学
|
Academic Significance and Societal Importance of the Research Achievements |
機能性材料ゼオライトを触媒として利用していく際の最大の課題は、構造・組成の安定性に影響する脱アルミニウムをいかに抑制できるかである。deNOx触媒として期待されている小細孔CHA及びAEIゼオライトにおいてホスホニウムカチオンをOSDA及びリン修飾剤とする合成法により、実用化の点からまだ十分と言えるレベルではないが、耐熱/耐水熱安定性を向上できることを明らかにした。ゼオライト合成に関する研究は世界で活発に行われ、筆者らのゼオライト水熱転換法を含む合成技術に関する新たな発見が続いており、高耐久性ゼオライトの設計・合成が近い将来可能になると期待している。
|