2018 Fiscal Year Final Research Report
Corrosivity of Magnesium Alloy for Biological Usage by Microstructure Control
| Project/Area Number |
16K05974
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Multi-year Fund |
|---|
| Section | 一般 |
|---|
| Research Field |
Materials/Mechanics of materials
|
|---|
| Research Institution | Shibaura Institute of Technology (2018)
University of Yamanashi (2016-2017) |
|---|
Principal Investigator |
|
|---|
| Research Collaborator |
MacDonald BryanJ.
|
|---|
| Project Period (FY) |
2016-04-01 – 2019-03-31
|
| Keywords | 生体吸収性マグネシウム合金 / 腐食挙動 / 表面性状 / 結晶粒微細化 |
|---|
| Outline of Final Research Achievements |
In recent years, magnesium is promising as a material for medical devices such as stents for a biological essential element. As applying magnesium alloy as a stent for cardiovascular stenosis, suppressing the extremely fast corrosion rate is a pressing issue. Therefore, in this research, it is regarded as a basic research, 1 investigation of surface characteristics of materials, 2 grain size / strain (dislocation density), 3 effects of blood flow on material corrosion, factors affecting corrosion rate it evaluated and showed the directionality not to solve the problem.
|
| Free Research Field |
材料力学・機械材料
|
| Academic Significance and Societal Importance of the Research Achievements |
ステントを体内吸収性材料を使用することで、取り出す再手術の負担を劇的に軽減できる。その有力な材料としてマグネシウム合金が挙げられる。マグネシウム合金は、体内必須元素であり、害はない。しかしながら、マグネシウム合金の強度や、腐食速度を制御しなければ、使用することはできない。そこで、強度や腐食を材料のパフォーマンスを生かして制御できれば、実用の可能性が大いに高まる。そこで、その各種条件、例えば、血流の流れ方、や形状の影響、一方で、材料の微細化による効果から、その材料の強度、腐食への影響を調査し明らかにした。
|