Ultra-morphological analysis of zirconia-veneering ceramic interface

2018 Fiscal Year Final Research Report

• Project/Area Number: 16K11622
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Research Field: Prosthodontics/ Dental materials science and
• Research Institution: Tokyo Medical and Dental University
• Principal Investigator: Kobayashi Kenichi 東京医科歯科大学, 歯学部附属病院, 講師 (00170316)
• Co-Investigator(Kenkyū-buntansha): 猪越 正直 東京医科歯科大学, 大学院医歯学総合研究科, 助教 (90753715)
• Project Period (FY): 2016-04-01 – 2019-03-31
• Keywords: ジルコニア / 陶材 / 界面

Outline of Final Research Achievements

The aim of this study was to clarify the zirconia-veneering ceramic interface using ultra-morphological analysis. Surface treatments (grinding, sandblasting) affected the crystal structure of zirconia. However, three surface treatment conditions (as-sintered, ground, sandblasted) resulted in comparable fracture strength of the zirconia-veneering ceramic interface. Ultra-morphological analysis revealed tight interface between zirconia and veneering ceramics.

Free Research Field

歯科補綴学

Academic Significance and Societal Importance of the Research Achievements

本研究では、臨床上遭遇することの多い、ジルコニア・陶材間の破折の原因を究明するため、ジルコニアへの表面処理の影響と、高解像度電子顕微鏡によるジルコニア・陶材界面の解析を行った。ジルコニアに対して表面処理を行うことで、ジルコニアの結晶構造が変化することが明らかとなった。さらに、この表面処理がジルコニア・陶材間の破折強度に与える影響は認められなかったことから、ジルコニアに陶材を築盛する際、表面処理を行う必要がない可能性が示唆された。