Development of new film and/or fiber materials using all the wood as raw material by applying biomass dissolution technology

2018 Fiscal Year Final Research Report

• Project/Area Number: 16K12648
• Research Category: Grant-in-Aid for Challenging Exploratory Research
• Allocation Type: Multi-year Fund
• Research Field: Design and evaluation of sustainable and environmental conscious system
• Research Institution: Kanazawa University
• Principal Investigator: Nishiwaki-Akine Yuri 金沢大学, 男女共同参画キャリアデザインラボラトリー, 特任助教 (80758277)
• Co-Investigator(Kenkyū-buntansha): 池本 良子 金沢大学, 地球社会基盤学系, 教授 (40159223)
• Project Period (FY): 2016-04-01 – 2019-03-31
• Keywords: バイオマス / セルロース / ヘミセルロース / リグニン / フィルム / 生分解性

Outline of Final Research Achievements

A new brown transparent woody film was developed by dissolving finely ground hardwood (Japanese beech) in formic acid at room temperature for 4 to 7 days, followed by slow evaporation of the solvent on the substrate. The film was bendable and could be folded without cracking like ORIGAMI with water. This film is almost the same component of wood itself, and it is foldable like paper because it contains cellulose (component of paper). The film was also water absorbent. The film had relatively high tensile strength and was mechanically and thermally stable up to 180 °C and did not soften. Furthermore, it had a very high biodegradability and it hardly retained its original form after 6 weeks buried in the soil at room temperature.