2017 Fiscal Year Final Research Report
Construction of synthesis process of copolymer with homogeneous composition and low polydispersity using ultrasonic irradiation
Project/Area Number |
16K14467
|
Research Category |
Grant-in-Aid for Challenging Exploratory Research
|
Allocation Type | Multi-year Fund |
Research Field |
Reaction engineering/Process system
|
Research Institution | Tohoku University |
Principal Investigator |
Kubo Masaki 東北大学, 工学研究科, 准教授 (50323069)
|
Project Period (FY) |
2016-04-01 – 2018-03-31
|
Keywords | 超音波 / コポリマー / 分子量分布 / 反応速度 / 反応工学 |
Outline of Final Research Achievements |
Poly (N-isopropylacrylamide-co-2-hydroxyethyl methacrylate) (P(NIPAM-co-HEMA)) was synthesized using ultrasonic irradiation in a mixed solvent of water and ethanol without chemical initiator. Effects of operational factors such as the monomer molar ratio and ultrasonic power intensity on time courses of the conversion ratio, the number average molecular weight, the polydispersity, and the copolymer composition of the synthesized polymers were investigated in order to determine the optimum conditions to synthesize the temperature-responsive polymer with low molecular weight distribution (i.e., low polydispersity). According to the experimental observation, a kinetic model for copolymer synthesis process under ultrasound was also constructed. The kinetic model can explain the experimental results of the conversion ratio, the number average molecular weight, the polydispersity, and the copolymer composition.
|