2007 Fiscal Year Final Research Report Summary
In situ Observation of the Coupling phenomenon between Iron Oxide and Carbon and the identification of the reaction species.
| Project/Area Number |
17360364
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Metal making engineering
|
|---|
| Research Institution | Hokkaido University |
|---|
Principal Investigator |
KASHIWAYA Yoshiaki Hokkaido University, Graduate School of Eng., Associate Prof. (10169435)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
ISHII Kuniyoshi Emeritus of Hokkaido University, Professor (00001214)
KINOSHITA Hiroshi Hokkaido University, Graduate School of Eng., Assistant Prof. (40177895)
|
|---|
| Project Period (FY) |
2005 – 2007
|
| Keywords | Coupling reaction / Quantification of coupling reaction / Direct reaction between iron oxide and carbon |
|---|
| Research Abstract |
In the present year, following new experiments were carried out and several new results were obtained. Those resu lts will be published in the future.
The new experiments
(1) Carbon ion implantation into hematite was carried out.
(2) XPS measurement on the hematite was carried out to clarify the variation of chemical bonding among Fe-C-O.
(3) In situ observation of high temperature behavior of the carbon implanted into hematite were preformed.
From these experiments, Chemical bonding among Fe-C-O atoms in the hematite were gradually changed from the surface. The existence of C-C bond showed a maximum value around 1μm to 2μm, the proportions of C-O bonding and C=O bonding were relatively high. In the region deeper than 2μm, Fe-C bonding was increased, which meant that the carbon implanted into hematite increased the interaction with Fe atom rather than O atom.
|
Research Products
(4 results)