Electrodeposition of refractory metals using ionic liquids in an intermediate temperature range

2019 Fiscal Year Final Research Report

• Project/Area Number: 17H03429
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Single-year Grants
• Section: 一般
• Research Field: Material processing/Microstructural control engineering
• Research Institution: Kyoto University
• Principal Investigator: Miyake Masao 京都大学, エネルギー科学研究科, 准教授 (60361648)
• Co-Investigator(Kenkyū-buntansha): 池之上 卓己 京都大学, エネルギー科学研究科, 助教 (00633538) ; 平藤 哲司 京都大学, エネルギー科学研究科, 教授 (70208833)
• Project Period (FY): 2017-04-01 – 2020-03-31
• Keywords: イオン液体 / 電析 / めっき / 高融点金属

Outline of Final Research Achievements

We demonstrated that dense and smooth tungsten alloy films can be electrodeposited using an ionic liquid as a solvent and a novel tungsten salt as an ion source. It was revealed that the resulted alloy films have high corrosion resistance and good mechanical properties. Through this work, we gained knowledge about the dissolution behavior of various tungsten salts in ionic liquids, the electrochemical behavior of tungsten ions in ionic liquids, and the effects of trace amounts of water on them.