A Study on the Shear Strength of Reinforced Concrete Cast-in-place Pile using Low Quality Recycled Aggregate Concrete with Vinylon Fiber

2019 Fiscal Year Final Research Report

• Project/Area Number: 17K06656
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Research Field: Building structures/Materials
• Research Institution: Nihon University
• Principal Investigator: MOROHASHI Noritaka 日本大学, 生産工学部, 教授 (90220110)
• Project Period (FY): 2017-04-01 – 2020-03-31
• Keywords: 低品質再生骨材コンクリート / 場所打ち鉄筋コンクリート杭 / せん断強度 / 圧縮強度 / ビニロン繊維 / ひび割れ / 乾燥収縮 / 円柱供試体

Outline of Final Research Achievements

Shear strength of reinforced concrete cast-in-place pile using low quality recycled aggregate concrete with vinylon fiber was examined. As the result, first of all the compressive strength of the cast-in-pile was slighty increased by the vinylon fiver under axial loading test. No defference was obserbed in both final fracture behavior of the cast-in-pile by the different types of concrete. On the otherhand, occurrence of cracks in cast-in-place using vinylon fiber dispersed.

Free Research Field

建築構造学，鉄筋コンクリート構造，建設廃棄物利用，リサイクル工学

Academic Significance and Societal Importance of the Research Achievements

現在，骨材の出荷の実態をみると，再生骨材の出荷量は砕石の1割程度で大変少なく，また再生骨材の出荷量のうち道路用に対してコンクリート用は道路用と比較して非常に少ない。天然資源の枯渇の観点から低い品質の再生骨材であっても普通骨材と混合利用することで構造用部材に用いるコンクリート用としての適用が可能となれば,再生骨材の普及につながり天然資源の維持に貢献できるものと考える。構造学的な観点から行った実験結果は，構造設計に再生骨材を用いたコンクリートを適用する際の安全性が示されたので再生骨材の需要拡大につながるものと考える。