Development of a vectorial induction device for biomedical tissues using high-resolution magnetic circuit

2020 Fiscal Year Final Research Report

• Project/Area Number: 17K20081
• Research Category: Grant-in-Aid for Challenging Research (Exploratory)
• Allocation Type: Multi-year Fund
• Research Field: Biomedical engineering and related fields
• Research Institution: Tohoku University
• Principal Investigator: Yukyo Takada 東北大学, 歯学研究科, 准教授 (10206766)
• Co-Investigator(Kenkyū-buntansha): 清水 良央 東北大学, 歯学研究科, 助教 (30302152) ; 高橋 正敏 東北大学, 歯学研究科, 助教 (50400255)
• Project Period (FY): 2017-06-30 – 2021-03-31
• Keywords: γ相 / 窒素 / 固溶 / オーステナイト / フェライト / 磁気回路 / レーザー / 組織誘導

Outline of Final Research Achievements

Although a magnetic/ non-magnetic hybrid structure could be obtained by laser drawing of ferritic XM27 stainless steel (Fe-26Cr-1Mo) that was treated with nitrogen solid solution at 1150℃, the generation of nitrogen gas and solidification shrinkage prevented expected result.
Then, we tried to manufacture a magnetic/ non-magnetic hybrid material using high-temperature masking treatment. Since a high-temperature masking material is indispensable, three samples such as an oxide film obtained by firing in the atmosphere, a commercially available high-temperature masking material, and a chromium oxide film were selected as masking materials, and their practicality in a high-temperature reducing atmosphere, was investigated. Among them, only the chromium oxide film which was obtained by firing a 5 μm chromium film at 900℃ no less than 30 minutes in the atmosphere, was stable even at high temperatures and showed a function of blocking nitrogen gas making the solid solution.