Production of ultra-refractory material with light weight by the surface modification of C/C composite with molten salt electrolysis

2020 Fiscal Year Final Research Report

• Project/Area Number: 18H01716
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Single-year Grants
• Section: 一般
• Review Section: Basic Section 26030:Composite materials and interfaces-related
• Research Institution: Tohoku University
• Principal Investigator: Takeda Osamu 東北大学, 工学研究科, 准教授 (60447141)
• Co-Investigator(Kenkyū-buntansha): 安田 幸司 京都大学, 工学研究科, 特定准教授 (20533665)
• Project Period (FY): 2018-04-01 – 2021-03-31
• Keywords: C/Cコンポジット / 耐熱材料 / 電解 / SiC / 電気化学

Outline of Final Research Achievements

In this study, the production of ultra-refractory material with a light weight that possesses significantly high endurance temperature was aimed by forming an oxidation resistance film on C/C composite that has not been commercialized. Following contents have been studied; the transportation rate of ions in molten salt, the rate of electrode reaction, the diffusion rate of atoms in solid electrode, the influence of electrolysis conditions on mechanical and chemical properties of coating film, the optimum formation conditions of coating film. The SiC coating film on C/C composite has been successfully formed by siliciding the surface of C/C composite with the developed surface modification method.

Free Research Field

溶融塩電気化学

Academic Significance and Societal Importance of the Research Achievements

本研究では、これまでAlやMg、レアアースといった活性金属の素材製造法に用いられてきた溶融塩電解法を耐熱材料の表面改質に適用することを実施し、耐酸化性皮膜の形成に成功した。これによって、溶融塩電解を用いた耐熱材料の表面改質という新しい学術分野の創出が期待される。また、本研究によって開発した表面改質法は、C/Cコンポジットによるタービンブレードの実用化に寄与すると期待される。超耐熱C/Cコンポジットが実用化されれば、コンバインドサイクルなどの火力発電のコストの大幅な削減が見込まれる。