Magnetic imaging using flexible magneto-optical imaging plate

2020 Fiscal Year Final Research Report

• Project/Area Number: 18H03776
• Research Category: Grant-in-Aid for Scientific Research (A)
• Allocation Type: Single-year Grants
• Section: 一般
• Review Section: Medium-sized Section 21:Electrical and electronic engineering and related fields
• Research Institution: Nagaoka University of Technology
• Principal Investigator: Ishibashi Takayuki 長岡技術科学大学, 工学研究科, 教授 (20272635)
• Co-Investigator(Kenkyū-buntansha): 西川 雅美 長岡技術科学大学, 工学研究科, 准教授 (20622393)
• Project Period (FY): 2018-04-01 – 2021-03-31
• Keywords: 磁気イメージング / 磁気光学効果 / 磁性ガーネット / 有機金属分解法 / 光MOD法 / 低温成膜技術 / 磁気光学イメージングプレート

Outline of Final Research Achievements

To realize a flexible magneto-optical imaging plate, we developed a low temperature preparation process for garnet films using the laser assisted metal-organic deposition method. The maximum process temperature for garnet films was successfully decreased from 650 to 450 degree C. A technique for deposition of MOD solutions using ultrasonic atomizer was developed, resulting that MOD solutions could be efficiently deposited on arbitary shaped materials. In addition, an MO imaging technique measuring 3D magnetic field distributions was successfully developed.

Free Research Field

磁気工学

Academic Significance and Societal Importance of the Research Achievements

本研究で開発した磁性ガーネット膜の低温成膜技術と超音波霧化法によるMOD溶液塗布技術が実現したことで、本研究の目的であるフレキシブル磁気光学イメージングプレートだけでなく、任意形状の測定対象物上に磁性ガーネットを直接形成することが可能になった。この成果は、これまで困難であった電動機などの複雑な形状の電流や磁場を可能にし、磁気イメージング技術を大きく進展させる成果である。また、薄膜の低温形成技術としても、様々な機能性材料の薄膜化へ応用が期待される