2020 Fiscal Year Final Research Report
Study on stripe-type antiferro magnetic cuprates with the two-leg ladder structure
| Project/Area Number |
18K03531
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Multi-year Fund |
|---|
| Section | 一般 |
|---|
| Review Section |
Basic Section 13030:Magnetism, superconductivity and strongly correlated systems-related
|
|---|
| Research Institution | Tohoku University |
|---|
Principal Investigator |
|
|---|
| Project Period (FY) |
2018-04-01 – 2021-03-31
|
| Keywords | 銅酸化物超伝導体 / 鉄系超伝導体 / 高圧合成 |
|---|
| Outline of Final Research Achievements |
In this study, we investigated the electronic properties of a copper oxide ACu2O3 with a two-legged ladder structure. By using a high-pressure synthesis method, we have established a method to prepare Mg1-xLixCu2O3, and have succeeded in extending the solid solution limit for Li from x = 0.12 to x = 0.60. The temperature dependence of the electrical resistivity in Mg1-xLixCu2O3 is insulator-like, despite the finite contribution of the electronic specific heat. This is due to the localization of the doped hole carriers, which is caused by the chemical disorder of the atomic sites.
|
| Free Research Field |
低温物理学
|
| Academic Significance and Societal Importance of the Research Achievements |
鉄系梯子型超伝導体と全く同じストライプ型反強磁性秩序を示す屈曲した梯子面を有する銅酸化物に関する研究を行なった．その結果，試料作製技術に関して，高圧合成法を用いることによって，従来困難であった高いホール濃度を実現する手法を確立した．また，広いホール濃度にわたって系統的な物性測定を実施したことによって，屈曲した梯子面を有する銅酸化物の電子状態に関する知見を得た．特に，原子サイトの乱れによって，ドープしたホールキャリアが局在化しており，この物質の電子状態に大きな影響を与えていることを明らかにした．
|