Bio-compatible Gold Plating for Tailored Tissue Regeneration and Neural Array Implants

2020 Fiscal Year Final Research Report

• Project/Area Number: 18K04736
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26030:Composite materials and interfaces-related
• Research Institution: Kanto Gakuin University
• Principal Investigator: CORDINIER CHRISTOPHER 関東学院大学, 材料・表面工学研究所, 研究員 (70724938)
• Co-Investigator(Kenkyū-buntansha): 福田 淳二 横浜国立大学, 大学院工学研究院, 教授 (80431675)
• Project Period (FY): 2018-04-01 – 2021-03-31
• Keywords: 無電解金めっき / 生体適合性 / 細胞シート形成 / 細胞シート転写

Outline of Final Research Achievements

On a 3 dimensional shaped substrate, a non-cytotoxic film was deposited from a bio-compatible electroless gold plating bath. Cell sheets were grown on the substrates then electrolytically transferred to a living system. This illustrated the application to related medical fields.

Free Research Field

表面工学、金化学

Academic Significance and Societal Importance of the Research Achievements

本研究では生体適合性無電解金めっきの開発を行った。樹脂製の基板を3Dプリンターによって作製し、金めっきを施したのち、表面に細胞を培養し細胞シートを形成した。細胞シートは電解剥離することができ、生体内に移植可能であることを示した。
生体適合性のある金めっき法を確立し、複雑な形状をした様々な基板材料に金めっきを形成することで、生体適合性無電解金めっきの可能性を示した。さらに、この方法を用いた細胞シートの作製により、医療分野への貢献が期待できる。