Development of the orientation control technique of the ZnTe epilayer on the sapphire substrate with facetted structure

2019 Fiscal Year Final Research Report

• Project/Area Number: 18K13792
• Research Category: Grant-in-Aid for Early-Career Scientists
• Allocation Type: Multi-year Fund
• Review Section: Basic Section 21050:Electric and electronic materials-related
• Research Institution: Tohoku University (2019); Waseda University (2018)
• Principal Investigator: Nakasu Taizo 東北大学, 多元物質科学研究所, 助教 (40801254)
• Project Period (FY): 2018-04-01 – 2020-03-31
• Keywords: II-VI族化合物半導体 / テルル化亜鉛 / サファイア / 分子線エピタキシー / 極点図法

Outline of Final Research Achievements

The preparation of the facetted sapphire substrate by annealing and the growth of the ZnTe epilayer on sapphire substrate with facetted structure by molecular beam epitaxy were investigated to control the orientation of the ZnTe epilayer on the sapphire substrate. The facetted structure was formed by the annealing when sapphire substrates with various orientations were used. It is possible to control the crystal orientation of the ZnTe epilayer by changing the off-angle of the (1-100) sapphire substrate.

Free Research Field

結晶工学

Academic Significance and Societal Importance of the Research Achievements

現段階では電磁波検出素子として他の半導体周辺回路と組み合わせが容易かつ安全な材料系はZnTeのみであると考えられ、本課題は電磁波検出の改善技術として重要な位置づけである。サファイア基板に生じるファセット構造を使った薄膜の配向制御により、ZnTeの成長方位に関する新たな知見を提供することで、これまでのGaN等のサファイア基板を用いたヘテロ成長に加え、様々な材料の結晶成長を可能とする重要な情報になると考えている。