2009 Fiscal Year Final Research Report
Novel fabrication of fine materials using liquid phase deposition process with Heterogeneous liquid-liquid interface
| Project/Area Number |
19205029
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (A)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Inorganic industrial materials
|
|---|
| Research Institution | Kobe University |
|---|
Principal Investigator |
DEKI Shigehito Kobe University, 工学研究科, 名誉教授 (10101065)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
MIZUHATA Minoru 神戸大学, 工学研究科, 准教授 (10283871)
KAJINAMI Akihiko 神戸大学, 環境管理センター, 准教授 (10169443)
|
|---|
| Project Period (FY) |
2007 – 2009
|
| Keywords | 液相析出法 / 逆相ミセル / 酸化チタン / アナターゼ / ナノ溶液 / 異相共存場 / 酸化スズ / 酸化物ナノ粒子 / 液-液界面 |
|---|
| Research Abstract |
The liquid phase deposition (LPD) of metal oxide thin films at the liquid-liquid interface was investigated. Just after the start of the LPD reaction, depositions were observed continually at the liquid-liquid interface. The deposition grew two-dimensionally into a self-standing film with thickness of 1・m and domain size of up to ca. 1mm without any solid substrates. The self-standing film was formed with asymmetrical morphology, which consisted of flat surface on the side of the liquid-liquid interface and relatively rough surface on the side of the bulk solution. The structure was characterized by Raman spectroscopy, confirming that metastable ammonium titanium oxide fluoride (NH_4TiOF_3) was first deposited at the liquid-liquid interface, on which anatase-type titanium oxide (TiO_2) was deposited second to forming the asymmetrical bilayer structure.
|
Research Products
(50 results)