2009 Fiscal Year Final Research Report
Fabrication of rare-earth doped transparent ceramics for white light sources and construction of evaluation system of optical properties
| Project/Area Number |
19350101
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Inorganic industrial materials
|
|---|
| Research Institution | Kyoto University |
|---|
Principal Investigator |
TANABE Setsuhisa Kyoto University, 大学院・人間・環境学研究科, 教授 (20222119)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
NISHI Masayuki 京都大学, 大学院・工学研究科, 助教 (50402962)
|
|---|
| Project Period (FY) |
2007 – 2009
|
| Keywords | 希土類 / 蛍光体 / 白色光源 / 透光性セラミックス / 蛍光スペクトル / 積分球 |
|---|
| Research Abstract |
We have carried out fabrication of rare-earth doped transparent ceramics for white light sources and constructed evaluation system of optical properties. Transparent ceramics with compositions of (Y_<0.99-x>Gd_xCe_<0.01>)_3Al_5O_<12> were prepared from nanopowders prepared by co-precipitation methods. Sintered ceramics with 1mm-thickness showed good transparency of 80% at 800nm and showed yellow photoluminescence by blue LED excitation (465nm). The peak wavelength of PLE shifted from 530nm to 560nm with increasing Gd content.
|
Research Products
(36 results)