2009 Fiscal Year Final Research Report
Fabrication of an oriented glass-ceramics electrolyte
| Project/Area Number |
19560681
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Inorganic materials/Physical properties
|
|---|
| Research Institution | University of Hyogo |
|---|
Principal Investigator |
MINESHIGE Atsushi University of Hyogo, 大学院・工学研究科, 助教 (00285339)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
YAZAWA Tetsuo 兵庫県立大学, 大学院・工学研究科, 教授 (50347522)
|
|---|
| Project Period (FY) |
2007 – 2009
|
| Keywords | アパタイト / イオン伝導体 / 燃料電池 / ガラスセラミックス |
|---|
| Research Abstract |
Oxyapatite-type La-Ca-Si-Al-O solid electrolytes were fabricated from melted glasses containing these oxides via crystallization process. Sliced glass plates were annealed in a furnace at above its crystallization temperature in order to obtain ceramics solid electrolytes. According to an XRD measurement, the main phase of the crystallized glass was oxyapatite, whose space group was the same as that for a high oxide-ion conductor, lanthanum silicates, La_<9.33+x>Si_6O_<26+1.5x>,. In addition, under certain conditions, an oriented ceramics exhibiting superior ionic conductivity could be obtained.
|