2009 Fiscal Year Final Research Report
High performance composite thermoelectric material with dispersed amorphous phase
| Project/Area Number |
19560729
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Material processing/treatments
|
|---|
| Research Institution | Osaka University |
|---|
Principal Investigator |
KATSUYAMA Shigeru Osaka University, 大学院・工学研究科, 准教授 (00224478)
|
|---|
| Project Period (FY) |
2007 – 2009
|
| Keywords | メカニカルミリング / メルトスピニング / ハーフホイスラー合金 / ゼーベック係数 / 電気抵抗率 / 熱伝導率 |
|---|
| Research Abstract |
The relationship between the microscopic structure and thermoelectric properties of half-Heusler ZrNiSn intermetallic compound was investigated. ZrNiSn_<0.98>Sb_<0.02>, which was partially substituted by Sb for Sn in ZrNiSn, was mechanically milled. The crystal grain size of the sintered body prepared from the milled powder decreased with an increase of the milling time, and the sample with a longer milling time showed a smaller thermal conductivity resulting in higher figure of merit. The reduction of the thermal conductivity was also observed in the composite sample with ZrNiSn crystal grain and ZrNi amorphous grain, and a slight increase of the figure of merit was observed. It became clear that there was a possibility of the enhancement of the figure of merit in the sample with dispersed amorphous phase.
|