2022 Fiscal Year Final Research Report
Development of resin impregnation method for CFRTP moulding using nano-carbon and elucidation of its mechanism
Project/Area Number |
19H02031
|
Research Category |
Grant-in-Aid for Scientific Research (B)
|
Allocation Type | Single-year Grants |
Section | 一般 |
Review Section |
Basic Section 18010:Mechanics of materials and materials-related
|
Research Institution | Doshisha University |
Principal Investigator |
TANAKA kazuto 同志社大学, 生命医科学部, 教授 (50303855)
|
Co-Investigator(Kenkyū-buntansha) |
片山 傅生 同志社大学, 研究開発推進機構, 嘱託研究員 (70161065)
森田 有亮 同志社大学, 生命医科学部, 教授 (80368141)
|
Project Period (FY) |
2019-04-01 – 2023-03-31
|
Keywords | 炭素繊維強化熱可塑性樹脂複合材料 / カーボンナノチューブ / ぬれ性 / 樹脂含浸 / 成形 |
Outline of Final Research Achievements |
Thermoplastic resins are expected to be used for matrix of fiber reinforced plastics due to the excellent recyclability and shorter production cycle time compared to thermoset resin. Since thermoplastic resins have a higher viscosity than thermosetting resin during the molding process, it is necessary to develop a method for impregnating resin into the carbon fiber bundle at the molding of carbon fiber reinforced thermoplastic (CFRTP). Grafting carbon nanotubes (CNTs) on the surface of carbon fibers improved not only the fiber/matrix interfacial shear strength but also the wettability. By using CNT grafted carbon fibers for reinforcement of CFRTP, CFRTP laminates with excellent impregnation can be obtained.
|
Free Research Field |
機械材料学
|
Academic Significance and Societal Importance of the Research Achievements |
繊維強化複合材料において,荷重を伝達する繊維樹脂界面特性の改善は重要な課題となる.ここでは,炭素繊維表面にカーボンナノチューブを析出させる手法を開発し,通常の炭素繊維と比べて繊維樹脂界面強度だけではなく,ぬれ性も改善できることを明らかにした.この開発したカーボンナノチューブ析出炭素繊維を用いることで,樹脂含浸特性に優れた炭素繊維強化熱可塑性樹脂複合材料の成形が可能であることを明らかにした.これらの材料を航空・宇宙機器や自動車をはじめとする輸送機器に採用することで,機体や装置の軽量化を実現することが可能となり,二酸化炭素排出量の削減に貢献することが出来る.
|