Study on Application of small-diameter drilling test to surface quality of concrete

2023 Fiscal Year Final Research Report

• Project/Area Number: 19K04719
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 23010:Building structures and materials-related
• Research Institution: Daido University
• Principal Investigator: FUJIMORI Shigeru 大同大学, 工学部, 准教授 (60437077)
• Project Period (FY): 2019-04-01 – 2024-03-31
• Keywords: 小径ドリル型削孔試験 / 削孔速度 / 表層品質評価 / 透気性 / 吸水性 / モルタル / コンクリート

Outline of Final Research Achievements

The purpose of this study is to establish a method to evaluate of surface layers such as permeability as well as strength by the small-diameter drilling test that has been developed for estimating compressive strength.
As a results, drilling speed obtained by the small-diameter drilling test could evaluate of the concrete surface layer and estimate compressive strength to the same degree as existing non-destructive and micro-destructive tests. And that air permeability of the surface layer could be evaluated with less damage by using the drilling test hole. Furthermore, it was shown that evaluate the amount of bleeding, air permeability, and water absorption, which affect the mass transport resistance of the concrete or mortar surface layer.

Free Research Field

建築材料，非破壊・微破壊試験，維持管理

Academic Significance and Societal Importance of the Research Achievements

研究成果より，小径ドリル型削孔試験機によって得られる削孔速度と各表層試験結果との対応関係を明らかとなった。その結果，現時点では限定的であるものの，小径ドリル型削孔試験によって得られる削孔速度によって，強度だけでなく，コンクリート表層の健全性の指標である，透気性，吸水性を評価できる可能性を示した。すなわち，非常に小さな損傷のみで，表層品質を評価できるということであり，新設構造物，歴史的建築物など，サンプルを採取することが難しい構造物においても，その品質評価が可能になることを示し，今後も増加し続けることが予想される，鉄筋コンクリート構造物の維持管理に大いに資するものと考えられる。