Study on Bar Coating of Metallic Lustrous Organic Crystals for Substitution of Metallic Paints

2021 Fiscal Year Final Research Report

• Project/Area Number: 19K05036
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26030:Composite materials and interfaces-related
• Research Institution: Tokyo University of Science
• Principal Investigator: Kondo Yukishige 東京理科大学, 工学部工業化学科, 教授 (70277276)
• Project Period (FY): 2019-04-01 – 2022-03-31
• Keywords: 金属フリー / 金色 / 銀色 / バーコーティング / 構造色

Outline of Final Research Achievements

After dissolving the compounds forming the gold or silver lustrous polycrystalline film in a good solvent, the compounds were precipitated as microcrystals by adding a poor solvent, and then the microcrystals were collected on filter paper by suction filtration. The remaining polycrystalline films of the compounds on the filter paper had a golden or silver luster. These polycrystalline films were ground until the metallic luster was intact, dispersed in a viscous polymer, i.e., polyvinyl alcohol (PVA)/boric acid mixture or sodium alginate (NaAlg)/calcium chloride mixture, and then successfully prepared into gold or silver lustrous sheets (~1 mm thick) by the bar coating method.

Free Research Field

界面化学

Academic Significance and Societal Importance of the Research Achievements

昨今、二酸化炭素の排出抑制を目指し、電気自動車 (EV) や燃料電池自動車 (FCV) の開発が盛んになされている。あわせて、電池から供給される電気エネルギーを効率的に自動車の駆動に利用するため、車重の軽量化も検討されている。申請者の金色・銀色多結晶膜は、メタリックペイントから得られる塗膜より、密度が低い。このため、車重の軽量化、ひいては電気エネルギーの効率的利用と二酸化炭素排出の抑制にも貢献できると期待される。
このような状況の中、申請者が有する、絶縁性の金属フリーな金属光沢多結晶膜は、上記の課題に対し一つの解を提供するものと期待される。