Osteoinduction of the cranial and spinal 3D-printed implants

2021 Fiscal Year Final Research Report

• Project/Area Number: 19K09517
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 56010:Neurosurgery-related
• Research Institution: Akita Cerebrospinal and Cardiovascular Center
• Principal Investigator: Sugawara Taku 秋田県立循環器・脳脊髄センター(研究所), 医工学研究部, 研究部長 (80241660)
• Project Period (FY): 2019-04-01 – 2022-03-31
• Keywords: チタン合金 / 骨誘導 / 3Dプリント

Outline of Final Research Achievements

3D-printed titanium alloy has an excellent physical strength, but other characteristics are unclear. Once heated, machine-cut titanium alloy is known to exhibit osteoinductive property by calcium ions attracted by the hydroxyl group on its surface, likewise 3D-printed materials may also have osteoinductive effects. In this study, best 3D-printing condition to induce bone induction is studied.

Free Research Field

脊椎脊髄外科

Academic Significance and Societal Importance of the Research Achievements

本研究で得られたデータは今後、骨補填・骨癒合を目的とするすべての3Dチタンプリンター造形物に応用できる基礎的なデータとなる。本研究では頭蓋骨・脊椎インプラントを想定しているが、人工歯根や人工関節など早期に強固な骨癒合が求められる他部位のインプラントについても応用可能である。多くの医療機器開発者・三次元造形物開発担当者が利用できるように、得られた研究結果は公開する。