Application of the Er:YAG-pulsed laser deposition method to the treatment of implant periodontitis

2022 Fiscal Year Final Research Report

• Project/Area Number: 19K10178
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 57040:Regenerative dentistry and dental engineering-related
• Research Institution: Osaka Dental University
• Principal Investigator: BABA Shunsuke 大阪歯科大学, 歯学部, 教授 (40275227)
• Co-Investigator(Kenkyū-buntansha): 岡村 友玄 大阪歯科大学, 歯学部, 講師 (10567473) ; 橋本 典也 大阪歯科大学, 歯学部, 教授 (20228430) ; 本津 茂樹 近畿大学, 生物理工学部, 研究員 (40157102)
• Project Period (FY): 2019-04-01 – 2023-03-31
• Keywords: Er:YAG レーザーデポジション法 / ハイドロキシアパタイト

Outline of Final Research Achievements

In this study, we aimed to simplify the technique of HAp coating on titanium
surfaces, then investigated the effects of HAp coating using an Er: YAG laser on titanium screws on the tissue　surrounding implant placement both in vitro and in vivo. These results showed that HAp can be deposited　more easily on titanium surfaces using an Er: YAG laser. It is also evident that HAp coating improved the induction of hard tissue differentiation and the formation of new bone in the tissue surrounding the implant　both in vitro and in vivo.

Free Research Field

再生歯学

Academic Significance and Societal Importance of the Research Achievements

本研究の結果より，Er:YAGレーザーを使用することによって，従来の方法より簡易に純チタン金属表面へのHAp 成膜が可能であることが明らかとなった．また，Er:YAG レーザーにより HAp を純チタン金属にコーティングすることによって，インプラント埋入周囲組織の硬組織分化誘導能および新生骨の形成を向上させることが，in vitro, in vivo両面から明らかとなった．本成果では新規のインプラント周囲炎に対する治療法に繋がる可能性を秘めており社会的意義は高い．