Elucidation and control of the formation mechanism of nanodomain structure

2020 Fiscal Year Final Research Report

• Project/Area Number: 19K15282
• Research Category: Grant-in-Aid for Early-Career Scientists
• Allocation Type: Multi-year Fund
• Review Section: Basic Section 26020:Inorganic materials and properties-related
• Research Institution: Tokyo Institute of Technology (2020); Tohoku University (2019)
• Principal Investigator: Shiraishi Takahisa 東京工業大学, 物質理工学院, 助教 (50758399)
• Project Period (FY): 2019-04-01 – 2021-03-31
• Keywords: 蛍石型酸化物 / 結晶相制御 / 電界印加 / 熱処理効果 / 歪制御

Outline of Final Research Achievements

The purpose of this study is to elucidate the formation mechanism of polar nanodomains contained in fluorite-type oxide films and to investigate the technique of their control. Focusing on strain, temperature, and electric field as control factors, we investigated structural changes due to each factor. First, we found the optimum buffer layer for strain control and succeeded in controlling the crystalline phase of the film. Next, in order to investigate the domain formation during the crystallization process, we obtained information on the formation process of the nanodomain structure by observing the structure of the film annealed at various conditions with a transmission electron microscope. Finally, we obtained knowledge about domain switching from the evaluation of electrical characteristics by applying an electric field.

Free Research Field

機能性酸化物膜の作製と物性解明

Academic Significance and Societal Importance of the Research Achievements

強誘電体蛍石型酸化物膜は、IoT社会の実現を支えるキーマテリアルとして注目されており、材料開発とデバイス開発が盛んにおこなわれている。しかし、実用に足る電気特性を達成するには種々の課題があり、その克服には膜の構造（特に、微細組織）制御に関する技術の確率が不可欠である。
本研究では、強誘電性の起源である直方晶相から成るナノドメインの制御を目的としており、得られた知見は材料設計およびデバイス設計を行う上で重要なものであるため、社会的意義は大きいと考えている。特に、温度と電界に対するナノドメイン構造の形成および変化に関する知見は、蛍石型酸化物群にとって普遍的なものであるため、学術的意義は大きい。