Research on optimal material properties of CAD/CAM crowns focusing on deformation behavior during fatigue.

2021 Fiscal Year Final Research Report

• Project/Area Number: 19K19083
• Research Category: Grant-in-Aid for Early-Career Scientists
• Allocation Type: Multi-year Fund
• Review Section: Basic Section 57050:Prosthodontics-related
• Research Institution: Tohoku University
• Principal Investigator: Harada Akio 東北大学, 歯学研究科, 助教 (40757267)
• Project Period (FY): 2019-04-01 – 2022-03-31
• Keywords: CAD/CAM / コンポジットレジン / 接着性レジンセメント / 弾性係数 / アコースティックエミッション

Outline of Final Research Achievements

The fracture strength of CAD/CAM generated composite resin crowns was evaluated to determine whether it is affected by the abutment tooth and type of luting cement. In addition to final fracture strength, initial fracture strength was evaluated by detecting acoustic emissions. Only the combination of metal abutment and composite resin cement showed significantly lower final fracture strength. On the other hand, initial fracture strength showed a different trend, with the combination of composite resin abutment and composite resin cement showing higher initial fracture strength for crowns and lower initial fracture strength for metal abutments. Considering the deformation behavior of the specimens under load, it is suggested that the combination of materials with similar modulus of elasticity might affect the initial fracture strength.

Free Research Field

CAD/CAMコンポジットレジン

Academic Significance and Societal Importance of the Research Achievements

日本ではCAD/CAM製レジンジャケットクラウン（以下CAD/CAM冠）が大臼歯に一部保険収載され、広く国民に適用されつつある。CAD/CAM冠は歯冠色を有しており、金属アレルギーのリスクがないとされる一方で、破折や脱離に関する懸念があり、臨床的にもトラブルが報告されている。特に大臼歯部においては破折に対する抵抗が重要と考えられ、クラウンが装着される支台歯やセメントなどの弾性係数が強度に影響すると考えられており、これらの環境について評価することが重要である。本研究成果より支台歯やセメントの弾性係数が強度に影響することが示唆されたが、リミテーションも多く、さらなる研究が必要である。