Synthesis of multi-block poly(substituted methylene)s

2020 Fiscal Year Final Research Report

• Project/Area Number: 19K22219
• Research Category: Grant-in-Aid for Challenging Research (Exploratory)
• Allocation Type: Multi-year Fund
• Review Section: Medium-sized Section 35:Polymers, organic materials, and related fields
• Research Institution: Ehime University
• Principal Investigator: Ihara Eiji 愛媛大学, 理工学研究科(工学系), 教授 (90243592)
• Project Period (FY): 2019-06-28 – 2021-03-31
• Keywords: ジアゾ酢酸エステル / ポリ（置換メチレン） / 末端官能化 / ブロック共重合体 / 機能性高分子

Outline of Final Research Achievements

We have established methods for quantitative incorporation of a functional group at a poly(substituted methylene) chain end. A hydroxy group was incorporated via termination with THF or H2O-mediated chain transfer, at a terminating or initiating chain end, respectively.
While the transformation of the hydroxy group to an azide group has not been achieved, we will try to realize it with more intensive optimization of the reaction conditions. Then, the chain end azide group will be utilized for the multi-block copolymer synthesis.
The chain end hydroxy group was successfully used as an initiating group for ring-opening polymerization of lactide to afford a block copolymer.

Free Research Field

高分子合成化学

Academic Significance and Societal Importance of the Research Achievements

ジアゾ酢酸エステルの重合によるポリ（置換メチレン）の合成は、炭素ー炭素結合を主鎖骨格とする高分子の新しい合成法として注目されている。この重合により得られるポリマーの末端に官能基を定量的に導入する手法の開発は、新しい機能性高分子の合成のための基礎研究として極めて重要である。今回、ポリ（置換メチレン）の開始および停止末端への水酸基の定量的な導入法の開発に成功した。その水酸基のアジド基への変換は期待通りには進行しなかったが、本研究を継続して工業的にも有用な新しい機能性高分子材料を開発することにより、社会に貢献することができる。