Development of New Corrosion Inhibition Technology for Localized Corrosion of Stainless Steel Using Chelating Incorporation Method

2020 Fiscal Year Final Research Report

• Project/Area Number: 19K23581
• Research Category: Grant-in-Aid for Research Activity Start-up
• Allocation Type: Multi-year Fund
• Review Section: 0401:Materials engineering, chemical engineering, and related fields
• Research Institution: Japan Atomic Energy Agency
• Principal Investigator: Aoyama Takahito 国立研究開発法人日本原子力研究開発機構, 福島研究開発部門 福島研究開発拠点 廃炉環境国際共同研究センター, 博士研究員 (60752623)
• Project Period (FY): 2019-08-30 – 2021-03-31
• Keywords: ステンレス鋼 / 腐食防食 / 局部腐食

Outline of Final Research Achievements

A method to use Cu2+ ions as corrosion inhibitors by chelating them as disodium copper(II) ethylenediaminetetraacetate ([Cu(EDTA)]Na2) was investigated. By conducting corrosion tests in solutions of sodium chloride (NaCl) with [Cu(EDTA)]Na2 and copper chloride (CuCl2), it was found that different effects occurred depending on the steel type and solution. It is thought that the pH of the solution changes the percentage of chelated Cu2+ ions and that inclusions in the steel have an effect.

Free Research Field

腐食防食

Academic Significance and Societal Importance of the Research Achievements

本研究では陽イオンである金属イオンをキレート化し、塩化物溶液中に添加することで、ステンレス鋼の局部腐食発生を抑制できることを見出した。このことにより、金属イオンを用いた新規腐食抑制剤の開発指針を得ることができた。金属元素を合金元素として鋼中に添加するのではなく、溶液中でキレート化するという観点の創出は腐食抑制剤の開発において貴重な提案であるといえる。