2010 Fiscal Year Final Research Report
Analysis of deformation behavior in SCC crack tip
| Project/Area Number |
20560621
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Physical properties of metals
|
|---|
| Research Institution | National Institute for Materials Science |
|---|
Principal Investigator |
NAGASHIMA Nobuo National Institute for Materials Science, 材料信頼性センター, 主任研究員 (30354252)
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
HAYAKAWA Masao 独立行政法人物質・材料研究機構, 材料信頼性センター, 主任研究員 (50354254)
ADACHI Yoshitaka 独立行政法人物質・材料研究機構, 材料信頼性萌芽ラボ, 主幹研究員 (90370311)
|
|---|
| Project Period (FY) |
2008 – 2010
|
| Keywords | 応力腐食割れ(SCC) / 微小硬さ / 原子間力顕微鏡 / SEM / EBSD |
|---|
| Research Abstract |
For the purpose of measuring strain distribution of the crack tip, the relations of the hardness and the strain were demanded. The hardness measurement performed Micro Vickers test (macrohardness), a microhardness test (meso hardness), nanoindentation test (nanohardness). As a result, it was evident that a microhardness examination was suitable for a measurement of the plasticity strain distribution of the crack tip. The crack propagation test out in air which simulated SCC crack propagation test was carried out. Crack tip of a provided specimen is plane strain condition. The strain distribution of the crack tip was able to be measured by the hardness distribution measurement of the microhardness test. In addition, as a result of having performed EBSD analysis about the crack tip of the specimen, a local direction difference produced the random grain boundary in the plastic deformation domain only in crack tip, and a local site direction difference didn't produce it in 3 Σ correspondence grain boundaries.
|