2022 Fiscal Year Final Research Report
Hierarchical structure and adhesion mechanism of metal/resin bonding interface revealed by advanced quantum beams
| Project/Area Number |
20H02455
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Review Section |
Basic Section 26030:Composite materials and interfaces-related
|
|---|
| Research Institution | Kyoto University (2020, 2022)
一般財団法人総合科学研究機構(総合科学研究センター(総合科学研究室)及び中性子科学センター(研究開発 (2021) |
|---|
Principal Investigator |
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
竹中 幹人 京都大学, 化学研究所, 教授 (30222102)
山本 勝宏 名古屋工業大学, 工学(系)研究科(研究院), 准教授 (30314082)
青木 裕之 国立研究開発法人日本原子力研究開発機構, 原子力科学研究部門 J－PARCセンター, 研究主幹 (90343235)
|
|---|
| Project Period (FY) |
2020-04-01 – 2023-03-31
|
| Keywords | 高分子吸着層 / 中性子反射率 / 高分子ダイナミクス / 量子ビーム / 耐湿信頼性 / ポリマー/フィラーナノコンポジット / 金属/樹脂接合材料 |
|---|
| Outline of Final Research Achievements |
In this project, in order to develop highly reliable metal/resin bonding technology, we used the latest quantum beams to clarify the hierarchical structure of the polymer layer adsorbed on an inorganic substrate, and to quantify the amount of the interfacial water accumulated at the interface between the polymer layer and substrate. The interfacial water is considered to cause bonding failure. As a result, the hierarchical structure of the adsorption layer within several nm from the interface was clarified by the neutron reflectivity (NR) method. It was found that the molecular chains within 1 nm from the interface were completely constrained on the substrate. Furthermore, we established a method to quantify the volume fraction of water in the interfacial region by NR under humidity conditions. Under high humidity over 85% RH, it was found that water with a maximum volume fraction of approximately 0.5 accumulates within 3 nm of the polypropylene/Si interface.
|
| Free Research Field |
高分子構造・物性
|
| Academic Significance and Societal Importance of the Research Achievements |
基板上の高分子吸着層の詳細な構造評価に、はじめて中性子反射率法を適用した。重水素化ポリマーを用いた吸着層の作製により、基板上の高分子吸着層は、これまで言われていた2層構造ではなく、3層構造をしていることが明らかになった。無機基板上に吸着した高分子の構造・ダイナミクス研究に大きな進展をもたらした。また調湿環境下でのポリマー/基板界面の水を比較的簡単に定量化できるようになった。これは材料の耐湿信頼性を予想する手法の確立につながることが期待される。
|