2022 Fiscal Year Final Research Report
Study of thick GaN crystals with low-dislocation density by the vapor phase epitaxy with an oxide gallium source
| Project/Area Number |
20H02639
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (B)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Review Section |
Basic Section 30010:Crystal engineering-related
|
|---|
| Research Institution | Osaka University |
|---|
Principal Investigator |
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
上殿 明良 筑波大学, 数理物質系, 教授 (20213374)
津坂 佳幸 兵庫県立大学, 理学研究科, 准教授 (20270473)
河村 貴宏 三重大学, 工学研究科, 助教 (80581511)
|
|---|
| Project Period (FY) |
2020-04-01 – 2023-03-31
|
| Keywords | OVPE / GaN / 低転位 / 低抵抗 |
|---|
| Outline of Final Research Achievements |
The objective of this study is to fabricate high-quality, thick GaN crystals by the oxide vapor phase epitaxy (OVPE) method and to measure the lattice parameter and defect density. By introducing a new hot-wall heater and increasing the amount of Ga source supplied, a high-speed growth rate of 300 um/h was achieved, and the problem of large pits was successfully suppressed. In the case of using a local heating system, a growth rate of 500 um/h was also achieved under high hydrogen concentration and high VIII ratio conditions. The lattice constant in the a-axis direction did not expand as much as expected despite the high oxygen impurity concentration, and epitaxial growth could be performed without any problem.
|
| Free Research Field |
結晶工学
|
| Academic Significance and Societal Importance of the Research Achievements |
現在、厚膜成長技術の主流として用いられているハイドライド気相成長（HVPE）法では結晶成長速度が200 μm/hと大きいのが特徴であるが、局所的な高酸素濃度領域を起点としてクラックが度々生じることが報告されているのに加え、転位密度は種結晶に依存する。一方、OVPE法は、ファセット成長により種結晶から転位密度が減少する機構を有している。また、酸素不純物が成長面に依存せず全面に含まれており、クラックが発生しづらいことから厚膜のバルクGaN結晶を安定的に供給できる可能性がある。本手法により低転位GaNウェハが安価で入手可能になり、GaN系デバイス分野の研究も飛躍的に進展することが期待される。
|