Development and biofunctionalization of novel endodontic cement of shape controlled complex oxides

2022 Fiscal Year Final Research Report

• Project/Area Number: 20H03869
• Research Category: Grant-in-Aid for Scientific Research (B)
• Allocation Type: Single-year Grants
• Section: 一般
• Review Section: Basic Section 57040:Regenerative dentistry and dental engineering-related
• Research Institution: Tokyo Medical and Dental University
• Principal Investigator: Uo Motohiro 東京医科歯科大学, 大学院医歯学総合研究科, 教授 (20242042)
• Co-Investigator(Kenkyū-buntansha): 稲田 幹 九州大学, 中央分析センター(筑紫地区), 准教授 (40624979) ; 小西 智也 阿南工業高等専門学校, 創造技術工学科, 教授 (90455163) ; 川島 伸之 東京医科歯科大学, 大学院医歯学総合研究科, 准教授 (60272605)
• Project Period (FY): 2020-04-01 – 2023-03-31
• Keywords: 歯科材料 / 歯内療法 / 歯科用セメント / イオン徐放 / X線造影性

Outline of Final Research Achievements

In this study, tristrontium aluminate (S3A) and distrontium cerate (S2Ce) were developed as the novel endodontic cement components. S3A and S2Ce showed shorter setting time compared to the commercial MTA cement. S2Ce showed higher compressive strength than the commercial MTA after 1 day of mixing. X-ray radiopacity of S3A was comparable to and that of S2Ce was three times higher than that of the commercial MTA, which contains the X-ray contrast agent. Dissolution of contrast agent might occur the discoloration of tooth. S3A and S2Ce cements developed in this study showed the feasibility to be a novel endodontic cement components which have both fast setting and high radiopacity.

Free Research Field

歯科理工学

Academic Significance and Societal Importance of the Research Achievements

近年、歯内療法用材料として注目されているMTAセメントはケイ酸三カルシウムを主成分とする。同セメントは歯内療法において優れた特性を持つが、X線造影性が低いため添加される造影剤の副作用が危惧されている。本研究で開発したストロンチウム(Sr)系セメントは優れた硬化特性とX線造影性を併せ持つため、新たなセメント成分として期待できる。加えて、Srイオンは硬組織再生などに優れた効果が示唆されており、上記新規セメント成分は歯内で高濃度にSrを放出して象牙質再生などに寄与する可能性があり、動物実験でもそれを示唆する結果が得られている。以上より本成果は歯内療法用セメント開発に寄与すると考えられた。