Micromechanical Analysis on Anisotropic Inclusion in Polymer Optical Fiber

2023 Fiscal Year Final Research Report

• Project/Area Number: 20K05098
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 26030:Composite materials and interfaces-related
• Research Institution: The University of Electro-Communications
• Principal Investigator: Furukawa Rei 電気通信大学, 大学院情報理工学研究科, 准教授 (50589695)
• Project Period (FY): 2020-04-01 – 2024-03-31
• Keywords: プラスチック光ファイバー / 異方性介在物 / 配向 / マイクロメカニックス / 動的散乱法

Outline of Final Research Achievements

In a system in which anisotropic inclusions are uniformly dispersed in the core of a polymer optical fiber, we investigated the orientation behavior of the internal anisotropic inclusions when deformations such as macrobending and normal stress are applied to the optical fiber.　　An experimental setup was prepared to characterize the orientation of anisotropic inclusions by detecting the polarization of an optical fiber. The results suggest that further reducing the inhomogeneity of the host optical fiber can enhance the signal from the orientation of the inclusion. The mechanism behind the inhomogeneity of the host optical fiber was also analyzed using dynamic scattering analysis.

Free Research Field

材料工学

Academic Significance and Societal Importance of the Research Achievements

プラスチック光ファイバーは１ミリ直径程度に太く製作しても、柔軟性を保つため、内部に微小物質を分散しても、一定以上の光量を伝送することができる。本研究では、プラスチック光ファイバー内に針状物質を分散し、ファイバー変形に伴いその針状物質が向きを変える挙動を調査した。このようなひずみに応じて向きを変える挙動は、センサー化したファイバーを使って、構造物の変形をモニタリングすることなどに役立つ可能性がある。今回は、その信号を出射偏波により検出し、得られた実験的データを使いマイクロメカニックスにより包括的に評価を試みた。結果として、検出信号をより顕著化するために母材の均一化が必要であることが示唆された。