Selective Recovery of Platinum Group Metals Based on Selective Ionic Crystal Formation and Preparation of Porous Catalysts

2023 Fiscal Year Final Research Report

• Project/Area Number: 20K05578
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 34030:Green sustainable chemistry and environmental chemistry-related
• Research Institution: Akita University
• Principal Investigator: Matsumoto Kazuya 秋田大学, 理工学研究科, 准教授 (70467025)
• Co-Investigator(Kenkyū-buntansha): 片桐 洋史 山形大学, 大学院理工学研究科, 教授 (40447206)
• Project Period (FY): 2020-04-01 – 2024-03-31
• Keywords: 白金族金属 / ロジウム / 白金 / イリジウム / イオン結晶 / 第一級アミン化合物 / 酸素発生触媒

Outline of Final Research Achievements

Quantitative and selective recovery of rhodium was successfully achieved by adding melamine, which is a primary amine compound with a heterocycle, to hydrochloric acid solutions containing platinum group metals. We also succeeded in quantitative and selective recovery of platinum by using 1,4-bis(aminomethy)lcyclohexane, an aliphatic primary diamine compound. It was revealed that the formation of ionic crystals is the key to selective recovery of the metals.
We succeeded in preparation of porous iridium oxide catalysts by calcination under air of ionic crystals composed of iridium and primary amine compounds. It was revealed that the porous iridium oxide catalysts obtained from ionic crystals using aniline exhibited excellent oxygen evolution catalytic ability.

Free Research Field

材料化学，複合化学

Academic Significance and Societal Importance of the Research Achievements

第一級アミン化合物を用いたイオン結晶形成に基づく新たな白金族金属選択回収法の開発に成功した。特にロジウムおよび白金については実用性の高い選択回収法であることを実証した。また，イオン結晶形成が選択回収の鍵となっていることを明らかにした。さらに，イリジウム含有イオン結晶は焼成により，多孔質酸化イリジウム触媒となることが判明した。作製した触媒は，市販品や過去の報告よりも優れた酸素発生触媒能を示すことが分かった。本研究の成果は，イオン結晶形成が選択回収技術としてだけでなく，新たな触媒作製技術としても応用できることを明らかにしており，リサイクル分野および触媒分野の発展に大きく寄与すると期待される。