2022 Fiscal Year Final Research Report
Development of stereo-triblock polydienes by organo rare-earth catalysts and mechanical properties of polydienes
| Project/Area Number |
20K05611
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Multi-year Fund |
|---|
| Section | 一般 |
|---|
| Review Section |
Basic Section 35010:Polymer chemistry-related
|
|---|
| Research Institution | Oyama National College of Technology |
|---|
Principal Investigator |
Nishii Kei 小山工業高等専門学校, 物質工学科, 准教授 (00552928)
|
|---|
| Project Period (FY) |
2020-04-01 – 2023-03-31
|
| Keywords | 1,3-ペンタジエン / イソタクチック / トランス-1,4 / リビング重合 / 熱可塑性エラストマー / イットリウム触媒 |
|---|
| Outline of Final Research Achievements |
Regio- and stereoselectivity control in the polymerization of 1,3-conjugated dienes is of much interest and importance. We report herein for the first time the isospecific trans-1,4-selective living polymerization of 1,3-pentadiene (PD) by a cyclopentadienyl-ligated yttrium catalyst/triphenylmethylium tetrakis(pentafluorophenyl)borate, which afforded crystalline isotactic-trans-1,4-polypentadiene showing good elastic properties without vulcanization (tensile strength up to 7.1 MPa with elongation at break of 2600%). Block copolymerization of PD and 1,3-butadiene (BD) has also been achieved to give novel isotactic-trans-1,4-polyPD-block-cis-1,4-polyBD copolymer by sequential monomer addition.
|
| Free Research Field |
高分子化学関連
|
| Academic Significance and Societal Importance of the Research Achievements |
PD重合で得られるポリPD（PPD）について、合成・ポリマー物性に関する報告は少ない．とくに，均一系触媒を用いたisotactic-trans-1,4-PPD（ITPPD）の合成例はなく，製品や用途開発が全く行われていない．よって，ITPPDの合成およびその物性評価で特長を見出すことができれば，現代社会で重要な工業材料になり得る．このため，ITPPDを合成することが高いチャレンジ性を有している．また，近年の環境問題や循環型社会の構築といった社会的ニーズという視点から，余剰C5留分の一部であるPDモノマーを有効利用し，TPEへ変換する本研究は「新規材料の創製」に大きく貢献できる．
|