2022 Fiscal Year Final Research Report
Fabrication of Copper-Tin based Semiconductor Photoelectrode for Transformation of Water and Carbon-dioxide Resources
| Project/Area Number |
20K05673
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Multi-year Fund |
|---|
| Section | 一般 |
|---|
| Review Section |
Basic Section 36010:Inorganic compounds and inorganic materials chemistry-related
|
|---|
| Research Institution | Osaka Institute of Technology |
|---|
Principal Investigator |
|
|---|
| Project Period (FY) |
2020-04-01 – 2023-03-31
|
| Keywords | p型化合物半導体 / 銅－スズ硫化物 / Cu2SnS3 / 水の光分解 / 水素製造 / 光電極 / 単斜晶相 / Sn-rich CTS |
|---|
| Outline of Final Research Achievements |
Copper tin sulfide (Cu2SnS3, CTS), a non-toxic p-type semiconductor composed of abundant elements in the earth crust has been employed for photoelectrochemical (PEC) water splitting. The CTS photoelectrodes were prepared by the electrodeposition (ED) of Cu and Sn ions with different Coulomb charge, followed by heating at 560°C in the presence of solid sulfur. The CTS photoelectrode with different Cu/Sn composition has a monoclinic structure, and it exhibits optical absorption from visible-light to infrared light having a bandgap of ca. 0.90 eV. The Pt-In2S3/CTS photoelectrode was demonstrated to generate H2 by the photocatalytic water splitting under solar light irradiation. Moreover, it was found that the PEC properties strongly depend on the Cu/Sn composite ratio of CTS, and the Sn-rich CTS exhibited the high PEC water splitting to produce H2.
|
| Free Research Field |
光電気化学
|
| Academic Significance and Societal Importance of the Research Achievements |
無尽蔵でクリーンな太陽光エネルギーと光触媒を用いて、水からの「グリーン水素」の製造により化学燃料へと物質循環するシステムの構築は、エネルギー・環境保全の観点から意義のある課題である。元素戦略の観点から、ベースメタルから構成される銅－スズ硫化物 (Cu2SnS3, CTS) 化合物半導体 は、高いモル吸光係数を有し、可視光から近赤外光を効率よく吸収できる光機能性材料として注目されている。CTS 薄膜は、専ら、電子ビーム蒸着法などの真空プロセスで作製される。設備コストを格段に下げるために、非真空プロセスによる、溶液から超低コストでの作製技術の確立が重要である。
|