Fundamental research for strong biological sealing between laminin electrodeposition dental metal implant and adherent epithelium

2022 Fiscal Year Final Research Report

• Project/Area Number: 20K10008
• Research Category: Grant-in-Aid for Scientific Research (C)
• Allocation Type: Multi-year Fund
• Section: 一般
• Review Section: Basic Section 57040:Regenerative dentistry and dental engineering-related
• Research Institution: Tokyo Medical and Dental University
• Principal Investigator: Nakaishi Michiko (寺田) 東京医科歯科大学, 生体材料工学研究所, 技術職員 (60374550)
• Project Period (FY): 2020-04-01 – 2023-03-31
• Keywords: 歯科金属インプラント / ラミニン / 電着 / 付着上皮 / 生物学的封鎖

Outline of Final Research Achievements

The electrodeposition of laminin to a titanium (Ti) surface and the orientation of laminin by a flow velocity using a rotating disk electrode becomes a biomimetics and makes metals l biofunctionalization, is aim of this study. The adjusted pH4 electrolyte and the direct current to apply cathode potential is a very effective for the laminin electrodeposition to the titanium surface. And there was no significant difference in the electrodeposition time. There was not the orientation of laminin by a rotating disk electrode. The electrodeposition was increased. However, it is considered that the control of the electrodeposition and the orientation of laminin needs detailed and severe conditions.

Free Research Field

歯科口腔外科

Academic Significance and Societal Importance of the Research Achievements

ラミニンが一様に、また、配向性をもってチタン表面に電着固定し、生体模倣の状態でチタンが生体機能化されることを予想していたが、本研究では、ラミニンは凝集体として散在していた上、配向性が認めらずに電着固定化されていた。しかしながら、より細かな条件でさらに研究を進めることで予想していた結果に近づける可能性もある。将来的には、ラミニンの工学的に汎用されている電着技術プロセスを生物学的に応用することのみならず、歯科から医科の領域にも応用できる可能性があり、将来的に広範に汎用できる技術を提供できる。