Clarification of high-strengthening mechanism of deformation-induced martensite based on dislocation engineering

2021 Fiscal Year Final Research Report

• Project/Area Number: 20K15050
• Research Category: Grant-in-Aid for Early-Career Scientists
• Allocation Type: Multi-year Fund
• Review Section: Basic Section 26040:Structural materials and functional materials-related
• Research Institution: Kyushu University
• Principal Investigator: Masumura Takuro 九州大学, 工学研究院, 助教 (40804688)
• Project Period (FY): 2020-04-01 – 2022-03-31
• Keywords: 加工誘起マルテンサイト / マルテンサイト / 転位密度 / 準安定オーステナイト / ステンレス

Outline of Final Research Achievements

In Fe-18Cr-8Ni alloy (SUS304), which is metastable austenitic stainless steel, the microstructure, hardness, and dislocation density of as-quenched and deformation-induced martensite were compared. The hardness and dislocation density of deformation-induced martensite are higher than those of as-quenched martensite, because the deformation-induced martensite is formed from work-hardened austenite with high dislocation density. On the other hand, the dislocation components (edge dislocations or screw dislocations) and the dislocation distribution were almost same between the deformation-induced and the as-quenched martensite.

Free Research Field

鉄鋼材料の組織制御

Academic Significance and Societal Importance of the Research Achievements

本研究は、高強度鋼として一般的に用いられる焼入れマルテンサイトと、TRIP鋼などで用いられる加工誘起マルテンサイトの強度と組織を比較したものである。従来、これら２つの組織の特性の違いが評価された例はなく、加工誘起マルテンサイトのほうが転位密度および硬さが高いという新たな知見が得られた。より高強度な鉄鋼材料を作製する上で、加工誘起マルテンサイトの利用価値が高いという結果は、工業的に大きな意義があると考えられる。