Effect of hydro-thermal treatment for adhesive primer

2023 Fiscal Year Final Research Report

• Project/Area Number: 20K18637
• Research Category: Grant-in-Aid for Early-Career Scientists
• Allocation Type: Multi-year Fund
• Review Section: Basic Section 57050:Prosthodontics-related
• Research Institution: Kyushu University
• Principal Investigator: Haraguchi Takuya 九州大学, 歯学研究院, 共同研究員 (20778865)
• Project Period (FY): 2020-04-01 – 2024-03-31
• Keywords: 水熱処理 / チタン合金

Outline of Final Research Achievements

A hydrothermal treatment (HT) of titanium with calcium (Ca) chloride solution was evaluated in this study. The adsorptions of both laminin-332 and osteopontin onto the Ca-HT surface were enhanced. In contrast, the adsorption of albumin was not influenced by Ca-HT. Osteoblast adhesion onto Ca-HT was also enhanced. Ca-HT had no impact in the adhesion of Streptococcus gordonii. These results suggest that Ca-HT enhances cell adhesion onto titanium without increasing bacterial adhesion, and the improvement of ECM protein adsorption is supposed to contribute to cell adhesion. When treated in HT-Ca, CaTiO3 like chemical component was observed on the titanium alloy surface.

Free Research Field

歯科補綴学

Academic Significance and Societal Importance of the Research Achievements

チタン合金は歯科用金属材料として広く臨床で用いられている。また、金属に高温、高圧の水の存在下で処理（水熱処理）を行うことで、性状が変化することが知られている。
水熱処理は比較的低温で起こる反応であり、安全に簡便な機器で処理できるため、その効果や作用機序を明らかにすることは実用性の観点からも社会的意義が高いと考えられる。また、水熱処理で金属表面に起こる反応は解析が困難であったが、今回、カルシウム水熱処理を行った際に、チタン酸カルシウムであると考えて矛盾しない化合物の生成を確認できた。このことは水熱処理反応の実態を解明する上で大きな学術的意義をもつと考えられる。