2023 Fiscal Year Final Research Report
Development of novel multi-caloric materials
| Project/Area Number |
20K20547
|
|---|
| Research Category |
Grant-in-Aid for Challenging Research (Pioneering)
|
| Allocation Type | Multi-year Fund |
|---|
| Review Section |
Medium-sized Section 26:Materials engineering and related fields
|
|---|
| Research Institution | Kyoto University |
|---|
Principal Investigator |
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
後藤 真人 京都大学, 化学研究所, 助教 (10813545)
市川 能也 京都大学, 化学研究所, 技術職員 (70365691)
|
|---|
| Project Period (FY) |
2020-07-30 – 2024-03-31
|
| Keywords | 熱量効果 / 遷移金属酸化物 / 1次相転移 / 熱制御 |
|---|
| Outline of Final Research Achievements |
In this study, we focused on novel materials exhibiting calorimetric effects. We found that the A-site ordered quadruple perovskite NdCu3Fe4O12 exhibited a large latent heat near room temperature due to a first-order phase transition caused by an intersite-charge-transfer transition. We further demonstrated that the observed giant entropy change associated with this phase transition can be utilized as a barocaloric effect by applying pressure. We also succeeded in synthesizing the ferrimagnetic oxide, BiCu3Cr4O12, which exhibited both a magnetic transition and a charge disproportionation transition simultaneously. The compound was found to exhibit multiple caloric effects where significant heat can be controlled by applying both pressure and a magnetic field.
|
| Free Research Field |
固体化学、材料科学
|
| Academic Significance and Societal Importance of the Research Achievements |
本研究の社会的意義は、近年、熱に関する問題がさまざまな形で顕在化する中で、社会からも強く解決が求められている冷房・冷却技術に対し、熱量効果を示す新材料により熱制御が可能であることを実証したことである。学術的には、電荷‐スピン‐格子が強く相関した物質系における電荷転移においては、重畳した巨大なエントロピー変化が起こるという新規なメカニズムを発見した。さらにこのような物質系は、熱を電場、磁場、圧力という複数の外場で制御できるマルチ熱量効果材料として機能させることができることも実証した。得られた一連の成果は大きな熱量効果を示す新材料の開発指針を示すものである。
|