Elucidation of electrodeposition mechanism on metallic glass film
| Project/Area Number |
21550188
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Inorganic industrial materials
|
|---|
| Research Institution | University of Yamanashi |
|---|
Principal Investigator |
SHIBATA Masami 山梨大学, 大学院・医学工学総合研究部, 教授 (40115316)
|
|---|
| Project Period (FY) |
2009 – 2011
|
| Keywords | 電気化学 / 機能性ガラス |
|---|
| Research Abstract |
The composition of the electrodeposited Pd-Ni-P films was controlled by adjusting the current density and the composition of Pd-Ni-P bath. The electrodeposited Pd-Ni-P films are metallic glass with Pd, Ni, and P compositions of 36-57at%, 25-43at%, and 17-20at%, respectively, which were almost identical to those in bulk Pd-Ni-P metallic glass. The alloy composition of the electrodeposited Pd_<42> Ni_<37> P_<21> metallic glass film was very similar to that of Pd_<40> Ni_<40> P_<20>, which is one of the best bulk metallic glasses because of its glass forming ability.
|