2011 Fiscal Year Final Research Report
Atomic bonding nature in aperiodic long-range ordered structures
| Project/Area Number |
21560003
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Applied materials science/Crystal engineering
|
|---|
| Research Institution | Hokkaido University |
|---|
Principal Investigator |
|
|---|
| Co-Investigator(Kenkyū-buntansha) |
ISHIMASA TSUTOMU 北海道大学, 大学院工学研究院, 教授 (10135270)
KASHIMOTO Shiro 北海道大学, 大学院・工学研究院, 助教 (60329852)
|
|---|
| Co-Investigator(Renkei-kenkyūsha) |
TSI An pang 東北大学, 多元物質科学研究所, 教授 (90225681)
YAMAMOTO Akiji 物質・材料研究機構, 名誉フェロー (90344431)
|
|---|
| Project Period (FY) |
2009 – 2011
|
| Keywords | 結晶工学 / 解析・評価 / 結晶成長 / 金属物性 |
|---|
| Research Abstract |
To give the basis of the aperiodic-crystal engineering, for quasicrystals and related approximant crystals, single crystal growths and crystal structure analyses have been attempted in several alloy systems. Single crystals, with a typical size of several millimeters of a decagonal phase with 1.6 nm periodicity and approximant crystals in the Al-Ni-Ru system were grown successfully by the flux method. Single crystals of a higher-order, 3/2-2/1, approximant to a decagonal phase with 1.2 nm periodicity have also been grown successfully. The flux method makes possible to grow single crystals of Al-based quasicrystals, which contain high-melting-point metal as constituent elements, at relatively low-temperatures.
|