2011 Fiscal Year Final Research Report
Creation of Wire Electrical Discharge Machined Surface without Cracks in Cemented Carbide
| Project/Area Number |
21560112
|
|---|
| Research Category |
Grant-in-Aid for Scientific Research (C)
|
| Allocation Type | Single-year Grants |
|---|
| Section | 一般 |
|---|
| Research Field |
Production engineering/Processing studies
|
|---|
| Research Institution | Niigata University |
|---|
Principal Investigator |
TAMURA Takeo 新潟大学, 自然科学系, 准教授 (90115048)
|
|---|
| Project Period (FY) |
2009 – 2011
|
| Keywords | 超硬合金 / ワイヤ放電加工 / 溶融再凝固層 / クラックレス / SI-cut / 表面改質 |
|---|
| Research Abstract |
As a method of processing cemented carbide, wire electrical discharge machining(WEDM) is generally used. However, typical surface defects, such as cracks, microcraters and recast layer, lead to a decreased surface integrity. Thus, an on-the-machine surface modification technology in WEDM, for the complete elimination of surface defects, was developed in this study. As a result, the surface defects generated by WEDM could be completely eliminated by incorporating SI-cut into WEDM. Thus, this surface modification technology is effective for finishing cemented carbide machined by WEDM.
|